“Efectos del Peróxido de Hidrógeno al 25% y luz

Ultravioleta sobre la Micromorfología Superficial del Esmalte”.


“Effects of 25% Hidrogen Peroxide and Ultraviolet light on the

Superficial Micromorphology of the Enamel”.


AUTORES
Dr. Felipe Tapia Lobos *
Dr. José Ricardo Tapia Silva (Mg) **
Dra. Ximena Zamorano Pino **
Dr. Vladimir Valenzuela Aránguiz (Mg)***

*Alumno Postítulo Especialización en
Rehabilitación Oral. Facultad de Odontología,
Universidad Mayor Santiago, Chile.
**Docentes Asignatura Odontología
Integral del Adulto. Facultad de Odontología,
Universidad Mayor Santiago, Chile.
***Profesor Asignatura Odontología
Integral del Adulto. Facultad de Odontología,
Universidad Mayor Santiago, Chile
.

 

 

RESUMEN
SUMMARY

Para determinar el efecto del peróxido de hidrógeno al 25% y luz ultravioleta sobre la micromorfología superficial del esmalte, se utilizaron 60 muestras de esmalte sano provenientes de terceros molares, divididos en cuatro grupos de 14 y tratados durante 40 y 60 minutos. La mitad de las muestras fueron tratadas con fluoruro de sodio al 1.1% por 5 min, para evaluar su efectividad después del blanqueamiento. Para el análisis micromorfológico se utilizó un microscopio electrónico de barrido (MEB), realizando observaciones a 100x, 500x, 1000x y 2000x. Los resultados fueron comparados cualitativamente respecto a los controles con el análisis de varianza de Kruskal-Wallis, evidenciándose diferencias significativas según el tiempo de exposición al agente blanqueador. Se concluyó que este sistema produce alteraciones en la micromorfología de la capa superficial del esmalte, y la aplicación de flúor durante 5 minutos posterior al tratamiento, no produce efectos substanciales en la remineralización del tejido expuesto.

Palabra Clave: Peróxido de hidrógeno al 25%, Luz ultravioleta, Micromorfología superficial del esmalte.

 

To determine the effect of 25% hydrogen peroxide and ultraviolet light on the superficial micromorphology of the enamel, we used 60 samples of healthy enamel taken from third molars. These samples were divided in four groups of 14 and exposed during 40 and 60 minutes. Half of the samples were treated with sodium fluoride 1.1% during 5 minutes to evaluate its effectiveness after dental bleaching. A scanning electron microscope was used for micromorphologic analysis, making observations at 100x, 500x, 1000x and 2000x. The results were compared cualitatively with the control samples using the Kruskal-Wallis analysis of variance. Significative diferences were evident according to the time interval of exposure to the bleaching agent. We concluded that this bleaching system produces alterations on the micromorphology of the superficial layers of the enamel, and that the aplication of sodium fluoride 1.1% during 5 minutes after treatment does not produce substancial effects on the remineralization the exposed tissue.

Key words: 25% Hydrogen Peroxide, Ultraviolet light, superficial micromorphology of the enamel.